Imec news

Archive 2008

IMEC reports new promising method to fabricate ultra-thin silicon solar cells

15/07/2008

SEMICON WEST 2008 – July 15-17, 2008 – Moscone Center – San Francisco – California – Booth #851

Leuven, Belgium – July 14, 2008 – IMEC is developing a new method to produce ~50μm thin crystalline silicon wafers for use in solar cells. The process involves mechanically initiating and propagating a crack parallel to the surface of a Si wafer. In this way, Si foils with an area of 25cm² and a thickness of 30-50μm have already been produced. The method makes use of industrially available tools (screen printer, belt furnace) and is potentially kerf-loss free.

Adding an ultra-thin wafer or foil of active silicon on top of a low-cost substrate is a promising solution to reduce the amount of high-grade silicon used in solar cells. IMEC is pursuing different paths to produce such foils of crystalline Si at an acceptable cost. One of the promising methods is a lift-off process that only requires the use of a screen printer and a belt furnace; no ion-implanted or porous layer is needed.

A metallic layer is screenprinted on top of a thick crystalline Si wafer, which is then annealed in a belt furnace at a high temperature. When the wafer cools, the mismatch of the thermal expansion coefficient between the metal and the silicon induces a stress field in the substrate.

The stress field grows, initiating and propagating a crack in the silicon, close to and parallel with the surface. Next, the top layer of the silicon and the attached metal layer snap off from the parent substrate. The metal layer is removed from the silicon foil in a metal-etching solution, resulting in a clean and stress-free ultra-thin silicon foil. The substrate can be re-used to peel off further layers.

The process was demonstrated on both single- and multi-crystalline silicon, as well as on Cz (Czochralski or a method of crystal growth used to obtain single crystals of semiconductors) material with different orientations. IMEC already produced foils with an area of 25cm2 and a thickness of 30-50μm.

One of the resulting thin Cz foils was further processed into a solar cell using a heterojunction emitter process. The 1cm² cell reached an efficiency of 10.0%, without back-surface passivation or intentional surface texturing. These preliminary results indicate that the quality of the material is largely preserved during the lift-off process, in spite of the large stresses involved. IMEC expects to reach much higher efficiencies with added surface passivation and texturing.

---ends---

Thermo-mechanical model of the lift-off process.

Ultra-thin crystalline Si foil; this side shows the surface cut from the thicker substrate.

About IMEC

IMEC is a world-leading independent research center in nanoelectronics and nanotechnology. IMEC vzw is headquartered in Leuven, Belgium, has a sister company in the Netherlands, IMEC-NL, offices in the US, China and Taiwan, and representatives in Japan. Its staff of more than 1600 people includes more than 500 industrial residents and guest researchers. In 2007, its revenue (P&L) was EUR 244.5 million.

IMEC’s More Moore research aims at semiconductor scaling towards sub-32nm nodes. With its More than Moore research, IMEC looks into technologies for nomadic embedded systems, wireless autonomous transducer solutions, biomedical electronics, photovoltaics, organic electronics and GaN power electronics.

IMEC’s research bridges the gap between fundamental research at universities and technology development in industry. Its unique balance of processing and system know-how, intellectual property portfolio, state-of-the-art infrastructure and its strong network worldwide position IMEC as a key partner for shaping technologies for future systems.

Further information on IMEC can be found at www.imec.be.



Back to overview